The work is devoted to the experimental verification of the assumption about the possibility of the generation of electroluminescence (EL) during the anodizing of metals in various alcohols as independent "water-like" electrolytes containing hydrosogroups. For example of metals from Al and Ta, anodized at a voltage of 1.2 kV for the first time, shows the possibility of their anodizing in ethyl, butyl, isobutyl, isoamyl alcohols, and also dimethylethanolamine and ethylene glycol. EL is registered in each of the listed alcohols. It is established that the magnitudes of its brightness-kinetic parameters depend on the geometrical and structural characteristics of the oxides formed. In alcohols, the hydrocarbon radicals of which contain several hydroxo groups or the reactivity of such a group is influenced by a different chemical element replacing carbon in the hydrocarbon radical, the highest densities of current flowing through the electrolyte are noted. The possibility of studying the EL and the anodizing processes occurring without any additives in the initial electrolyte solutions is shown, which simplifies the interpretation of the results.

На примере анодов из Al и Ta при напряжении 1,2~kV показана возможность их анодирования в чистых спиртах и генерация при этом процессе электролюминесценции (ЭЛ), что исключает необходимость учета каких-либо добавок в исходных растворах электролитов и упрощает интерпретацию результатов исследований этого явления. У спиртов, углеводородные радикалы которых содержат несколько гидроксогрупп, или на реакционную способность такой группы оказывает влияние иной химический элемент, замещающий углерод в углеводородном радикале, отмечены наиболее высокие плотности протекающего через электролит тока.