The research of parameters of formation of domain structure in lithium niobate with gradient of concentration
UDC
621.373Abstract
For the experimental research of process of formation of domain structure in lithium niobate with gradient of concentration the focused crystal plate of 0.4 mm (a so-called z-cut, i.e. the allocated axis of the crystal is perpendicular plate planes) has been used in the thickness. Put during crystal pulling up time the gradient of structure of the plate of lithium niobate along an axis x was close to linear and changed at level of 2% (from $R=0.94$ to 0.96). Crystal repolarization was made by the appendix to a thin plate of a high voltage. Peak value made 7 kV. Reflection of domain formation processes in electric field time change of values of the field necessary for repolarization is. From experimental data, follows that formation of domain structure in the crystal lithium niobate with gradient of concentration occurs practically at one value of the polarizing pressure brought to a crystal plate. And, the current starts to proceed through a plate at excess of level of pressure 6.5 kV that makes 16.5 kV/mm. Certainly, the given value is the integrated parameter characterizing all plate of lithium niobate entirely. However the strongly pronounced beginning of formation of domains testifies, as well as it was supposed about insignificance of influence of a gradient of structure of a plate in the borders specified above under condition of replacement of defects "niobium in lithium site" ions non-photorefractive impurity.
Keywords:
lithium niobate, regular domain structure, polarizationAcknowledgement
References
- Wang Jian, Fu Hongyan, Geng Dongyu, Willner Alan E. Single-PPLN-assisted wavelength-/time-selective switching/dropping/swapping for 100-GHzspaced WDM signals. Optics Express, 2013, vol. 21, no. 3, pp. 3756-3774.
- Sidorov N.V., Volk T.R., Mavrin B.N., Kalinnikov V.T. Niobat litiya: defecti, fotorefrakciya, kolebatelniy spektr, polyaritoni [Niobate of lithium: defects, photorefraction, vibration spectrum, polaritons]. Moscow, Nauka Publ., 2003, 250 p.
- Johnston Benjamin F. Fabrication and characterisation of poled ferroelectric optical crystals. Macquarie University: Thesis for the degree of Doctor of Philosophy, 2008, 236 p.
- Galutskiy V.V., Vatlina M.I., Stroganova E.V. Growth of single crystal with a gradient of concentration of impurities by the Czochralski method using additional liquid charging. Journal of Crystal Growth, 2009, vol. 311, pp. 1190-1194.
- Galutskiy V.V., Stroganova E.V., Shmargilov S.A., Yakovenko N.A. Frequency conversion in compositionally graded PPLN crystals. Quantum Electronics, 2014, vol. 44, no. 1, pp. 30-33.
Downloads
Issue
Pages
Submitted
Published
How to Cite
Copyright (c) 2015 Galutskiy V.V., Stroganova E.V., Shmargilov S.A., Tsema A.A., Yakovenko N.A.
![Creative Commons License](http://i.creativecommons.org/l/by/4.0/88x31.png)
This work is licensed under a Creative Commons Attribution 4.0 International License.